Standards
| TS EN ISO 14174 | SA CS/MS 1 68 AC |
|---|---|
| EN IS014174 | SA CS/MS 1 68 AC |
| AWS A5.17 | F6AZ-EL12 / F6A0-EM12 |
Chemical Composition of Weld Metal % (Typical)
| SAW — Wire | C | Si | Mn |
|---|---|---|---|
| S1 | 0.05 | 0.80 | 1.10 |
| S2 | 0.04 | 0.45 | 1.27 |
Mechanical Properties
| SAW Wire | AWS A5.17 | Yield Strength (N/mm²) | Tensile Strength (N/mm²) | Elongation ((Lo=5do) (%)) | Impact Strength (ISO-V/ 0°C) | Impact Strength (ISO-V/-20°C) (Joule) |
|---|---|---|---|---|---|---|
| S1 | F6AZ-EL12 | 395 | 475 | 24 | 38 J | — |
| S2 | F6A0-EM12 | 390 | 485 | 30 | — | 69 J |
Features and Applications
- A type of SAW flux structured from agglomerated manganese silicate and calcium silicate
- Basicity of the flux according to Boniszewski formula is 1.0
- Weld beads of excellent surface appearance and with easily removed slags
- High resistance to porosity caused by oil and rust
- High capacity of current flow
- Suitability for use in 2-pass welding operations on thick materials (best choice for base metals in thicknesses of 10-40 mm)
- Requirement of re-drying at 250-350°C for 2 hours
Operating Data
| Product Code | Package Weight (Kg) | Package Type |
|---|---|---|
| 3010800009 | 25 | Kraft Bag |